Product Details:
Shape | L shape |
Color | Silver |
Usage/Application | Industrial |
Grade | EN 8D |
Length | 3-6 meter |
Material | Steel |
Technique | Hot Rolled |
Thickness | Upto 12 mm |
Properties | Metric | Imperial |
---|---|---|
Hardness, Brinell (typical) | 300 | 33 |
Hardness, Rockwell C (typical) | 30 | 30 |
Tensile strength, ultimate | 965-1030 MPa | 140000-150000 psi |
Tensile strength, yield |
827-862 MPa | 120000-125000 psi |
Elongation at break (in 50 mm (2")) | 20.0% | 20.0% |
Compressive strength | 862 MPa | 125000 psi |
Charpy impact (V-Notch) | 27.1-33.9 J | 20.0-25.0 ft-lb |
Poisson's ratio | 0.27-0.30 | 0.27-0.30 |
Elastic modulus | 190-210 GPa | 27557-30457 ksi |
Min U.T.S.on Drawingt kg/mm2 | Mechanical Properties after heat treatment | Typical Appilications | ||
---|---|---|---|---|
U.T.S | Y.S | Elong %min. | ||
Kg/mm2 min | ||||
62 | 63 | 44 | . | Dynamos and motor shafts heat treated bolts,connecting rods and crankshafts |