Product Details:
| Product Type | Carbon Steel Pipes |
| Wall Thickness | 3-7 mm |
| Material | Carbon Steel |
| Size | 2 inch |
| Surface Treatment | Polished |
| Unit Pipe Length | 3-6 meter |
| Shape | Round |
| Material Grade | Ck 20 |
| Usage/Application | Industrial |
Product Details:
| Product Type | Carbon Steel Pipes |
| Wall Thickness | 3-7 mm |
| Material | Carbon Steel |
| Size | 1-2 inch |
| Surface Treatment | Polished |
| Unit Pipe Length | 3-6 meter |
| Shape | Round |
| Material Grade | Ck 30 |
| Usage/Application | Industrial |
Product Details:
| Product Type | Carbon Steel Pipes |
| Wall Thickness | 3-7 mm |
| Material | Carbon Steel |
| Size | 2 inch |
| Surface Treatment | Polished |
| Unit Pipe Length | 3-6 meter |
| Shape | Round |
| Material Grade | Ck 35 |
| Usage/Application | Industrial |
Product Details:
| Wall Thickness | 3-7 mm |
| Material | Carbon Steel |
| Size | 2 inch |
| Surface Treatment | Polished |
| Unit Pipe Length | 3-6 meter |
| Material Grade | Ck 45 |
| Shape | Round |
| Usage/Application | Industrial |
Product Details:
| Product Type | Carbon Steel Pipes |
| Wall Thickness | 3-7 mm |
| Material | Carbon Steel |
| Size | 2 inch |
| Surface Treatment | Polished |
| Unit Pipe Length | 3-6 meter |
| Shape | Round |
| Material Grade | C40 |
| Usage/Application | Industrial |
Product Details:
| Product Type | Carbon Steel Pipe |
| Wall Thickness | 3-7 mm |
| Nominal Pipe Size | 3-6 meter |
| Material Grade | 60C8 |
| Usage/Application | Industrial |
| Material | Carbon Steel |
| Technique | Hot Rolled |
Carbon steels have carbon as the key alloying element in their composition. They also contain up to 0.4% silicon and 1.2% manganese. In addition, the residual elements such as copper, molybdenum, aluminium, chromium and nickel are present in these steels.
Mechanical Properties:
| Properties | Metric | Imperial |
| Tensile strength Ultimate | 660 MPa | 95700 psi |
| Tensile strength Yield | 560 MPa | 81200 psi |
| Bulk modulus (typical for steels) | 140 GPa | 20300 ksi |
| Shear modulus (typical for steels) | 80 GPa | 11600 ksi |
| Elastic modulus | 190 - 210 GPa | 19700- 30458 ksi |
| Poisson’s ratio | 0.27 -0.30 | 0.27 - 0.30 |
| Elongation at break (in 50 mm) | 0.1 | 0.1 |
| Reduction of area | 0.4 | 0.4 |
| Hardness, Brinell | 197 | 197 |
| Hardness, Knoop (converted from Brinell hardness) | 219 | 219 |
| Hardness, Rockwell B (converted from Brinell hardness) | 92 | 92 |
| Hardness, Rockwell C (converted from Brinell hardness. Value below normal HRC range, for comparison purposes only) | 13 | 13 |
| Hardness, Vickers (converted from Brinell hardness) | 207 | 207 |
| Machinability (based on AISI 1212 steel. as 100 machinability) | 55 | 55 |
| Properties | Metric | Imperial |
| Density | 7.85 g/cm3 | 0.284 lb/in³ |
| Properties | Metric | Imperial |
| Thermal expansion co-efficient | 11 µm/m°C | 6.11 µin/in°F |
| Thermal conductivity | 49.8 W/mK | 346 BTU in/hr.ft².°F |