Carbon Steel

Our range of products include is2062e250a carbon steel, c40 carbon steel, c 60 carbon steel, ck 30 carbon steel, en32b carbon steel and c 15 carbon steel.

IS2062E250A Carbon Steel

IS2062E250A Carbon Steel
  • IS2062E250A Carbon Steel
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Yield Strength250 MPa minimum
Tensile Strength410 MPa minimum
Elongation23% min.
Bend Test3t (min) for E-250 Gr. A & 2t (min) for E-250 Gr. B
Charpy TestApplicable for E-250-B quality & thickness of 12mm & above

IS 2062 E250 mild steel plates to be welded using CO 2 as shielding gas. Welding speed is select as process variable while arc voltage, welding current, wire feed rate distance between the nozzle and the plates are fixed in this experiment. The effect of weld speed on the weld bead profile is been discussed with the effect of weld speed on the fusion angle and wetting angle. The effect of weld speed on the weld bead dilution i.e. penetration area and reinforcement area also be discussed.

Product Details:

Grade Carbon Equivalent (max)
IS 2062 E250 A0.42
IS 2062 E250 B0.41
IS 2062 E250 C0.39
IS 2062 E410    0.44
IS 2062 E450 D0.46
IS 2062 E450 E0.48
IS 5986 Fe4100.42
Request
Callback
Yes! I am Interested

C40 Carbon Steel

C40 Carbon Steel
  • C40 Carbon Steel
Get Best Quote
Approx. Price: Rs 55 / KilogramGet Latest Price

Product Details:

ApplicationIndustrial
MaterialCarbon Steel
GradeC40
Length Per RodUpto 100 Meter

We are a well-renowned organization in the industry to provide our patrons the best quality array of C40 Carbon Steel.
Request
Callback
Yes! I am Interested

C 60 Carbon Steel

C 60 Carbon Steel
  • C 60 Carbon Steel
Get Best Quote
Approx. Price: Rs 60 / KilogramGet Latest Price

Product Details:

ApplicationIndustrial
MaterialCarbon Steel
GradeC60
ThicknessUpto 7 mm

Being a leading enterprise of this industry, we are offering a huge range of C 60 Carbon Steel
Request
Callback
Yes! I am Interested

Ck 30 Carbon Steel

Ck 30 Carbon Steel
  • Ck 30 Carbon Steel
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Modulus of elasticity200 [10^3x N/mm2]
Density7.85 [lbs/in3]
Specific heat Capacity0.486
Thermal Conductivity51.2

This is a higher carbon (0.30%) manganese steel in the plain carbon steel alloy family. It provides greater strength than the lower carbon grades while still retaining reasonable ductility.

Designation by Standards:

  • Brand Name: Ck 30
  • Mat No1.1178
  • DIN Ck30
  • EN -AISI 1030


Applications:

  • CK30 steel is generally used in the quenched and tempered condition for strength. Applications include machinery parts where strength and hardness are requisites.
  • Physical Properties(average values) at ambient temperature

Soft Annealing:
  • A full anneal is accomplished at 870 to 980°C followed by slow cooling in the furnace.
  • A stress relief anneal may be done at 540°C.

Hardening:
  • Heat treat at 810 to 870°C and water quench, followed by a tempering treatment.

Tempering:
  • Temper, after heat treat and quench, at 320 to 540°C depending upon strength level desired

Forging:
  • Hot forming temperature: 1050-850°C.

Machinabilty:
  • Machinabilty of CK30 steel is rated at 70% that of the AIS11112 steel considered to be 100% machinable as a reference.

Corrosion Resistance:
  • This is a plain carbon steel and will rust unless protected.

Welding:
  • CK30 steel may be welded by all methods.
  • In heavy sections it is advisable to pre-heat at 150 to 260°C and post-heat at 540 to 650°C for welding.

Cold working:
  • Cold working of CK30 steel in the annealed condition may be don by conventional methods.
  • A fuU or stress relief anneal may be needed after cold working.


Chemical Composition:

GradeMinMax
Carbon, C0.250.35
Manganese, Mn0.600.90
Silicon, Si0.150.35
Sulfur, S-.--0.50
Phosphorous, P-.--0.50


Mechanical Properties of grade C30:

Nominal thickness (mm):0.3 - 3
Rm - Tensile strength (MPa) (+A)520
Nominal thickness (mm):0.3 - 3
Rm - Tensile strength (MPa) (+CR)920
Nominal thickness (mm):0.3 - 3
A - Min. elongation Lo = 80 mm (%) (+A)20
Vickers hardness ( HV): (+CR)270
Vickers hardness ( HV): (+A)165

 

Request
Callback
Yes! I am Interested

EN32B Carbon Steel

EN32B Carbon Steel
  • EN32B Carbon Steel
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Tensile Strength430 N/mm2
Elongation18%
Impact Izod J39
Impact KCV J35

EN32 is a carbon case hardening steel. Components when carburized have a core strength range of 430-490 N/mm2 , with a hard wearing surface. It is a popular case hardening steel grade for general engineering, readily machineable and weldeable in its supply condition. EN32 is a low tensile steel suited for lightly stressed components.

Applications:
  • Commonly used for general engineering lightly stressed applications that are subject to wear, EN32 is suitable for applications such as collets, cams, rollers, bushes, spindles, and gears.

Case Hardening:
  • Blank carburize EN32 at a temperature between 880-930°C. Refine at temperature of 970-900°C, cool in air, oil or water.
  • Hardening: Harden at a temperature of 760-780°C. Quench in water. Tempering
  • Tempering is recommended for stress relief and maximum case toughness. Tempering range from 150-200°C.

Heat Treatment:
  • Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each steel component.
  • Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult your heat treatment provider for full guidance on heat treatment of case hardening steel grades.
  • Forging: Heat slowly and uniformly to 1100°C. After forging cool slowly.
  • Annealing: Heat uniformly to 700°C. Soak well and cool slowly in the furnace Welding: Firstly heat to approximately 100-350°C.
  • Use an unalloyed basic electrode, for welding unalloyed structural steels. Normalising: Normalize at 840-870°C, and cool in air.
  • Stress Relieving: After rough machining tools should be stress relieved.
  • Soaking time 2 hours after the whole piece has attained a temperature of approximately 675°C. Cool in furnace to approximately 500°C, and then freely in air.

 

Chemical composition:

ElementMinMax
Carbon, C0.100.18%
Manganese, Mn0.701.10%
Silicon, Si0.050.35% 
Nickel, Ni-.---.--
Molybdenum, Mo-.---.--
Chromium,Cr-.---.--
Sulfur, S-.--0.07
Phosphorous, P-.--0.05
Request
Callback
Yes! I am Interested

C 15 Carbon Steel

C 15 Carbon Steel
  • C 15 Carbon Steel
Get Best Quote
Approx. Price: Rs 50 / KilogramGet Latest Price

Product Details:

ApplicationUsed for applications such as cold headed fasteners and bolts
MaterialCarbon steel
GradeC15

Being one of the trusted organizations in the market, we are affianced in providing a wide range of C 15 Carbon Steel.

Features:

  • Elevated durability
  • Corrosion proof
  • Fine finish
Request
Callback
Yes! I am Interested

Ck 30 Carbon Steel

Ck 30 Carbon Steel
  • Ck 30 Carbon Steel
Get Best Quote
Approx. Price: Rs 50 / KilogramGet Latest Price

Product Details:

ApplicationApplies to petroleum, chemical industry, electric power, etc.
MaterialCarbon Steel
GradeCk 30

We are a unique name in the market to provide our honorable customers an exclusive range of Ck 30 Carbon Steel.

Features:

  • Rugged design
  • High temperature resistance
  • Superior finish
Request
Callback
Yes! I am Interested

SAE And AISI 1035 Carbon Steel

SAE And AISI 1035 Carbon Steel
  • SAE And AISI 1035 Carbon Steel
Get Best Quote
Approx. Price: Rs 55 / KilogramGet Latest Price

Product Details:

ApplicationIndustrial
MaterialCarbon Steel
ThicknessUpto 8 mm

Being a leading enterprise in this industry, we are offering a huge range of SAE And AISI 1035 Carbon Steel.
Request
Callback
Yes! I am Interested

Ck 20 Carbon Steel

Ck 20 Carbon Steel
  • Ck 20 Carbon Steel
Get Best Quote
Approx. Price: Rs 50 / KilogramGet Latest Price

Product Details:

ApplicationShip building industry, Engineering, Pump and valve industry, etc.
MaterialCarbon Steel
GradeCK 20

In order to retain remarkable position in this industry, we are providing a wide array of C20 Carbon Steel.

Features:

  • Highly durable
  • Corrosion resistance
  • Excellent finish

Request
Callback
Yes! I am Interested

CK 35 Carbon Steel

CK 35 Carbon Steel
  • CK 35 Carbon Steel
Get Best Quote
Approx. Price: Rs 55 / KilogramGet Latest Price

Product Details:

ApplicationIndustrial
MaterialCarbon Steel
GradeCK 35

We are engaged in offering a quality approved range of Ck 35 Carbon Steel.

Features:

  • Rugged design
  • High temperature resistance
  • Superior finish

Applications:

  • Construction industry
  • Pipe line transport
  • Chemical towers
Request
Callback
Yes! I am Interested

Ck45 Carbon Steel

Ck45 Carbon Steel
  • Ck45 Carbon Steel
Get Best Quote
Approx. Price: Rs 60 / KilogramGet Latest Price

Product Details:

ApplicationIndustrial
MaterialCarbon Steel
GradeCK45

Being a leading enterprise of this industry, we are offering a huge range of Ck45 Carbon Steel
Request
Callback
Yes! I am Interested

S355J2G3 Carbon Steel

S355J2G3 Carbon Steel
  • S355J2G3 Carbon Steel
Get Best Quote
Approx. Price: Rs 60 / KilogramGet Latest Price

Product Details:

ApplicationIndustral
MaterialCarbon Steel
GradeS355J2G3

We are a well-renowned organization in the industry to provide our patrons the best quality array of S355J2G3 Carbon Steel
Request
Callback
Yes! I am Interested

EN43B Carbon Steel

EN43B Carbon Steel
  • EN43B Carbon Steel
Get Best Quote
Approx. Price: Rs 60 / KilogramGet Latest Price

Product Details:

ApplicationIndustrial
MaterialCarbon Steel
GradeEN43B

As a quality focused firm, we are engaged in offering a high-quality range of EN43B Carbon Steel
Request
Callback
Yes! I am Interested

EN32B Carbon Steel

EN32B Carbon Steel
  • EN32B Carbon Steel
Get Best Quote
Approx. Price: Rs 60 / KilogramGet Latest Price

Product Details:

ApplicationIndustrial
MaterialCarbon Steel
GradeEN32B

With immense market knowledge, we have been able to provide optimum quality EN32B Carbon Steel
Request
Callback
Yes! I am Interested

15C8 Carbon Steel

15C8 Carbon Steel
  • 15C8 Carbon Steel
Get Best Quote
Approx. Price: Rs 60 / KilogramGet Latest Price

Product Details:

ApplicationConstruction, Industrial
MaterialCarbon Steel
Grade15C8

Being one of the trusted organizations in the market, we are engaged in providing a wide range of 15C8 Carbon Steel
Request
Callback
Yes! I am Interested

30C8 Carbon Steel

30C8 Carbon Steel
  • 30C8 Carbon Steel
Get Best Quote
Approx. Price: Rs 60 / KilogramGet Latest Price

Product Details:

ApplicationConstruction, Industrial
MaterialCarbon Steel
Grade30C8

In order to retain remarkable position in this industry, we are providing a wide array of 30C8 Carbon Steel
Request
Callback
Yes! I am Interested

C45 Carbon Steel

C45 Carbon Steel
  • C45 Carbon Steel
Get Best Quote
Approx. Price: Rs 55 / KilogramGet Latest Price

Product Details:

ApplicationIndustrial
MaterialCarbon Steel
GradeC45

Being a leading enterprise of this industry, we are offering a huge range of C45 Carbon Steel
Request
Callback
Yes! I am Interested

SAE And AISI 1020 Carbon Steel

SAE And AISI 1020 Carbon Steel
  • SAE And AISI 1020 Carbon Steel
Get Best Quote
Approx. Price: Rs 55 / KilogramGet Latest Price

Product Details:

ApplicationIndustrial
MaterialCarbon Steel
ThicknessUpto 8 mm

We are remarkable enterprise, instrument in offering superior quality SAE And AISI 1020 Carbon Steel.
Request
Callback
Yes! I am Interested

C35 Carbon Steel

C35 Carbon Steel
  • C35 Carbon Steel
Get Best Quote
Approx. Price: Rs 55 / KilogramGet Latest Price

Product Details:

ApplicationIndustrial
MaterialCarbon Steel
ThicknessUpto 8 mm

Being a leading enterprise of this industry, we are offering a huge range of C35 Carbon Steel.
Request
Callback
Yes! I am Interested

EN 8 Carbon Steel

EN 8 Carbon Steel
  • EN 8 Carbon Steel
Get Best Quote
Approx. Price: Rs 55 / KilogramGet Latest Price

Product Details:

ApplicationIndustrial
MaterialCarbon Steel
GradeEN8

Being a leading enterprise of this industry, we are offering a huge range of EN 8 Carbon Steel
Request
Callback
Yes! I am Interested

CK 15 Carbon Steel

CK 15 Carbon Steel
  • CK 15 Carbon Steel
Get Best Quote
Approx. Price: Rs 60 / KilogramGet Latest Price

Product Details:

ApplicationConstruction
MaterialCarbon Steel
GradeCK15

Being a customer-oriented enterprise, we are engaged in providing a wide array of CK 15 Carbon Steel
Request
Callback
Yes! I am Interested

Carbon Steel 40C8

Carbon Steel 40C8
  • Carbon Steel 40C8
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Metric7.85 g/cc
Imperial0.284 lb/in3
Tensile strength Ultimate660 MPa

Carbon steels have carbon as the key alloying element in their composition. They also contain up to 0.4% silicon and 1.2% manganese. In addition, the residual elements such as copper, molybdenum, aluminium, chromium and nickel are present in these steels.

Mechanical Properties:
PropertiesMetricImperial
Tensile strength Ultimate660 MPa95700 psi
Tensile strength Yield560 MPa81200 psi
Bulk modulus (typical for steels)140 GPa20300 ksi
Shear modulus (typical for steels)80 GPa11600 ksi
Elastic modulus190 - 210 GPa19700- 30458 ksi
Poisson’s ratio0.27 -0.300.27 -0.30
Elongation at break (in 50 mm)0.10.1
Reduction of area0.40.4
Hardness, Brinell197197
Hardness, Knoop (converted from Brinell hardness)219219
Hardness, Rockwell B (converted from Brinell hardness)9292
Hardness, Rockwell C (converted from Brinell hardness. Value below normal HRC range, for comparison purposes only)1313
Hardness, Vickers (converted from Brinell hardness)207207
Machinability (based on AISI 1212 steel. as 100 machinability)5555

Thermal Properties:
PropertiesMetricImperial
Thermal expansion co-efficient11 µm/m°C6.11 µin/in°F
Thermal conductivity49.8 W/mK346 BTU in/hr.ft².°F

Physical Properties:
PropertiesMetricImperial
Density7.85 g/cm30.284 lb/in³
Request
Callback
Yes! I am Interested

C 15 Carbon Steel

C 15 Carbon Steel
  • C 15 Carbon Steel
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Brinell hardness98 - 178 (HBW) (+SH)
Silicon0.10%
Nominal thickness5-10 mm

C15 is a plain carbon steel with a nominal 0.15% carbon content. It is a relatively low strength steel but it may be quenched and tempered for increased strength.

Application:

  • The low carbon steels, such as C15 are used for applications such as cold headed fasteners and bolts.

Soft Annealing:
  • Heat to 850-950°C, cool slowly. This will produce a hardness of 90-100 HB.

Stress Annealing:
  • Stress relieving to remove machining stresses should be carried out by heating to approx.
  • 540°C, holding for 1-2 hours at heat, followed by air cooling.
  • This operation is performed to reduce distortion during heat treatment

Forging:
  • Hot forming temperature: 1200-950°C.

Corrosion Resistance
:
  • This is a plain carbon steel and has no corrosion resistance. It will rust unless protected.

Heat treatment conditions:
+ASoft annealed
+ACAnnealed to achieve spheroidization of the carbides
_+ARAs rolled
+ATSolution annealed
+CCold drawn / hard
+CRCold rolled
+FPTreated to ferrite-pearlite structure and hardness range
+IIsothermal annealing
+LCCold drawn / soft
+MThermo mechanical rolling
+NNormalized
+NTNormalized and tempered
+PPrecipitation hardened
+PEPeeled
+QAAir quenched and tempered
+QLLiquid quenched and tempered
+QTQuenched and tempered
+STreated to improve shearability
+SHAs rolled and turned
+SRCold drawn and stress relieved
+TTempered
+THTreated to hardness range
+WWWarm worked
+UUntreated

Chemical composition:
ElementMinMax
Carbon, C-.--0.20
Manganese, Mn-.--0.80
Silicon, Si-.--0.10
Sulfur, S-.--0.06
Phosphorous, P-.--0.06

Mechanical Properties:
Nominal thickness (mm)5 --1010--1616 -4040 -6363 -100
Rm - Tensile strength (MPa) (+C)500-800480-780430-730380-670340-600
Nominal thickness (mm)5 --1010--1616 -4040 -6363 -100
Rp0.2 0.2% proof strength (MPa) (+C)380340280240215
Nominal thickness (mm)5 --1010--1616 -4040 -6363 -100
A - Min. elongation at fracture (%) (+C)7891112

Physical Properties(avarage values) at ambient temperature:
PropertiesMetric
Modulus of elasticity [10^3x N/mm2]210
Density [g/cm3]:7.85
Thermal conductivity [W/m.11]58.6
Electric resistivity [Ohm mm2/m]:0.11
Specific heat capacity[lig.11]0.46
Request
Callback
Yes! I am Interested

C20 Carbon Steel

C20 Carbon Steel
  • C20 Carbon Steel
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Bulk modulus140 GPa
Yield strength360 MPa
Tensile strength425 MPa

C-20 is an unalloyed low carbon mild steel grade supplied as a hot rolled or bright drawn finish bar. As a low carbon steel grade it provides low strength with good machinability and is suitable for welding. Mild Steel, fairly easy to machine but with a tendency to ‘rip’ if unlubricated. It is very easy to weld and is used as a more general purpose steel for multiple applications.

Common Uses:
  • Lightly stressed bolts, fixings, shafts, spacers, hubs and bushings. Bracketry, linkages and base plates would be fine to produce using EN3.

Not Suitable For:
  • Stress components such as torque loaded shafts, high bending forces and shock loading.
  • The material will yield and distort under stress conditions, bending before shear.

Machining:
  • Surface ‘ripping’ is more evident in EN3 so lubrication is essential. Fairly high surface speeds should be used with moderate feeds.
  • Screw cutting is easy with cutting oil and achieving a fine finish is achieved with slight polishing. Very nice to weld with good flow and strength.

Annealing:
  • C-20 is commonly supplied bright drawn or as rolled. If annealing is required heat to 880-910°C, furnace cool.

Hardening:
  • As a low carbon steel C-20 is not ideally suited for heat treatment (EN8 or EN9 may be a better suited option).
  • If hardening is required heat to a temperature of 880-910°C. Quench in water and temper.

Heat Treatment:
  • When hardening C-20 heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each component.
  • Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities.
  • Please consult your heat treatment provider for full guidance on heat treatment of C-20 carbon steel.

Application:
  • Commonly used for general engineering C-20 is suitable for applications such as bolts, shafts, spaces, hubs, base plates, brackets. fixtures and jigs.

 

Chemical composition:

ElementMinMax
Carbon, C-.--0.25
Manganese, Mn-.--1.00
Silicon, Si0.050.35
Sulfur, S-.--0.06
Phosphorous, P-.--0.06

Thermal Properties:
propertiesMetricImperial
Thermal conductivity51.9 W/mK360 BTU in/hr.ft².°F

Mechanical Properties:
Mechanical PropertiesMetricImperial
Tensile strength425 MPa61600 psi
Yield strength360 MPa52200 psi
Bulk modulus140 GPa20300 ksi
Shear modulus80 GPa11600 ksi
Elastic modulus190-210 GPa27557-30458 ksi
Poisson's ratio0.27-0.300.27-0.30
Elongation at break0.150.15
Reduction of area0.40.4
Hardness, Brinell121121
Hardness, Knoop140140
Hardness, Rockwell B6868
Hardness, Vickers126126
Machinability6565
Request
Callback
Yes! I am Interested

Ck 20 Carbon Steel

Ck 20 Carbon Steel
  • Ck 20 Carbon Steel
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Thermal expansion16 - 17 e-6/K
Thermal conductivity16 - 16 W/m.K
Specific heat500 - 500 J/kg.K

CK-20 is a Fe-Cr-Ni alloy containing slightly more chromium and considerably more nickel than the CH-20 grade. The alloy is used provides good resistance to dilute sulfuric acid and resists many co rodents more effectively Than CF-8 type. The alloy is fully austenitic and contains chromium carbides throughout the matrix, which are put into solution by High temperature solution anneal, which also improves ductility and strength. The alloy should be solution Annealed to maximize corrosion resistance and after welding to prevent sensitization of the HAZ.

 

Applications:

  • Pump casings, valve bodies, digesters, roaster hardware..

Product Forms:
  • Horizontal and vertical centrifugal castings; static castings
  • Physical Properties(average values) at ambient temperature

Weldability:
  • CK-20 may be welded by the SMAW, GTAW and GMAW processes.
  • Electrodes 310
  • Preheat Not required
  • Post weld heat treatment 20000F W.Q.

Related Specifications:
  • Nearest wrought grade: AISI 310 .

 

Chemical Composition

ElementMinMax
Carbon, C0.400.50
Manganese, Mn0.600.90
Silicon, Si0.151.35
Sulfur, S-.--0.50
Phosphorous, P-.--0.50


Specifications:

PropertiesMetric
Modulus of elasticity [10^3x N/mm2]210
Density [lbs/in3]0.28
Magnetic Permeability1.02 (Soln Ann)
Thermal Expansion70-212oF 8.3
(10-6in/in oF) 70-600oF 8.9
70-1000oF 9.4
Thermal Conductivity7.9 @ 212°F
(Btu/h/ft2/ft/oF) 9.8 @ 600oF
11.8 @ 1000oF


Physical Properties:

QuantityValueUnit
Thermal expansion16 - 17e-6/K
Thermal conductivity16 - 16W/m.K
Specific heat500 - 500J/kg.K
Melting temperature1370 - 1400°C
Service temperature0 - 500°C
Density8000 - 8000kg/m3
Resistivity0.7 - 0.7Ohm.mm2/m


Thermal Properties:

Thermal Properties

Conditions


T (°C)Treatment
Thermal Conductivity (W/m-K)42.7100
@ 200 °C/392 °F47750-100
Request
Callback
Yes! I am Interested
View PDF

CK 35 Carbon Steel

CK 35 Carbon Steel
  • CK 35 Carbon Steel
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Modulus of elasticity210 [10^3x N/mm2]
Density7.86 [lbs/in3]

CK35 steel has a higher (0.35%) carbon content for greater strength than the lower carbon alloys. It is hardenable by heat treatment, quench and tempering to develop 150 to 250 ksi tensile strength.

 

Designation by Standards:

  • Brand Name: Ck 35
  • Mat No1.1181
  • DIN Ck35
  • EN -
  • AISI 1035


Applications:

  • Component parts for automobile industry, e.g., shafts, forgings, flanges, bushings, crankshafts, connecting rods and parts for the machine building industry.

Soft Annealing:
  • Heat to 650-700°C, cool slowly in furnace. This will produce a maximum Brinell hardness of 226.

Normalizing:
  • Normalizing temperature: 880-910°C.

Tempering:
  • Tempering from the quenched condition may be done at 550-660°C depending upon the strength desired

 

Forging:

  • Hot forming temperature: 1100-850°C.

Machinability:
  • Machinabilty of CK30 steel is rated at 70% that of the AIS11112 steel considered to be 100% machinable as a reference.

Cold Working:
  • In the annealed state the CK35 alloy is readily cold worked by conventional methods.

Corrosion Resistance:
  • This is a steel alloy and will rust if not protected. it is not corrosion resistant.

Welding:
  • CK35 steel is weldable by all of the welding methods. However with its higher carbon content it is important to use both pre-heat at 150 to 260°C and post-heat at 590 to 650°C practice per an approved welding procedure.

 

Chemical Composition:

ElementMinMax
Carbon, C0.300.40
Manganese, Mn0.600.90
Silicon, Si0.150.35
Sulfur, S-.--0.50
Phosphorous, P-.--0.50


Mechanical Properties in Normalized', Hardened+Tempered Condition:

Diameter (mm)0.2 % proof stress (Wmm 2 )Tensile strength (Wmm 2 )Elongation A5 (%)Reduction Z Impact (%) strength (J)
Up to 16*300*480-67021'

17-100*270*480-670*21'

101-160*245*460-650*19'

Upto 16430630-780174040
17-40370600-750194540
41-100320550-700205040

 

 

Request
Callback
Yes! I am Interested

Ck 40 Carbon Steel

Ck 40 Carbon Steel
  • Ck 40 Carbon Steel
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Modulus of elasticity210 [10^3x N/mm2]
Density7.84 g/cm3
Manganese0.90%

CK40 steel has a higher (0.40%) carbon content for greater strength than the lower carbon alloys. It is hardenable by heat treatment, quench and tempering to develop 150 to 250 ksi tensile strength.

 

Designation by Standards:

  • Brand Name: Ck 40
  • Mat No1.1186
  • DIN Ck40
  • EN -
  • AISI 1040


Applications:

  • Used for crankshafts, couplings and cold headed parts.
  • Physical Properties(average values) at ambient temperature

Soft Annealing:

  • Heat to 870-980°C, cool slowly in furnace.
Normalizing:

  • Normalizing temperature: 890°C.

Forging:

  • Hot forming temperature: 1100-850°C.

Machinability:

  • Machinability is good,rated at 60 % that of the AIS11112 alloy steel which is considered 100% machinable Corrosion Resistance
  • This is a steel alloy and will rust if not protected. it is not corrosion resistant Welding
  • CK40 steel is weldable by all of the welding methods. However with its higher carbon content it is important to use both pre-heat at 150 to 260°C and post-heat at 590 to 650°C practice per an approved welding procedure.

Tempering:
  • Tempering from the quenched condition may be done at 320-700°C depending upon the strength desired

Cold Working:

  • In the annealed state the CK 40 alloy is readily cold worked by conventional methods


Chemical Composition:

GradeMinMax
Carbon, C0.350.45
Manganese, Mn0.600.90
Silicon, Si0.150.35
Sulfur, S-.--0.50
Phosphorous, P-.--0.50


Mechanical Properties in Normalized', Hardened+Tempered Condition:

Normalized, +N:
Diameter d [mm]<16<16-40>40-100>100-160>160-250
Thickness<882060100
0,2%proof stress
Rpo,2 [MN/mm2]
min.320min.290min.260
Tensile strength Rmm [N/mm2
min580min.550min.530
Fracture elangonation A5 [%]min.16min.17min.17

 





Request
Callback
Yes! I am Interested

Ck 45 Carbon Steel

Ck 45 Carbon Steel
  • Ck 45 Carbon Steel
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Modulus of elasticity190 - 210 [10^3x N/mm2]
Density7.84 [lbs/in3]
Thermal Conductivity15.1 [W/m.K]

1045 is a medium carbon steel is used when greater strength and hardness is desired than in the as rolled’ condition. Extreme size accuracy, straightness and concentricity combine to minimize wear in high speed applications. Turned, ground and polished.


Designation by Standards:

  • Brand Name: Ck 45
  • Mat No1.1191
  • DIN Ck45
  • EN -
  • AISI 1045


Applications:

  • Component parts for vechiles, shafts, bushings, crankshafts, connecting rods and parts for the machine building industry and steel for axes, knives, hammers, etc
  • Physical Properties(average values) at ambient temperature

Chemical Composition:
ElementMinMax
Carbon, C0.400.50
Manganese, Mn0.600.90
Silicon, Si0.151.35
Sulfur, S-.--0.50
Phosphorous, P-.--0.50

Coefficient of Linear Thermal Expansion 10^-6 °C^-1:
20-100°C20-200°C20-300°C20-400°C20-500°C20-600°C20-700°C
11.612.313.113.714.214.715.1

Tempering temperature: See the data below:

20°C50°C100°C150°C200°C250°C300°C
56565654524945.5

Mechanical Properties Vs Diameter:
DiameterTensile Strength (MIDa)Yield Strength (MPa)Elongation Reduction (%) in Area (%)
Cold drawn, round bar (16-22 mm)6555851235
Cold drawn, round bar (32-50 mm)5855151030
Cold drawn, round bar (50 - 75mm)5154851030
Cold drawn, round bar (22-32 mm)6205501130
Cold drawn, round bar (19-32 mm)6255301230
Cold drawn, annealed, round bar (19-32 mm)5855051245
Cold drawn, high temperature, stress relieved, round bar (16-22 mm)6555151545
Cold drawn, high Temperature, stress relieved, round bar (50-75 mm)5504501235
Cold drawn, high temperature, stress relieved, round bar (32-50 mm)5854851540
Cold drawn, high temperature, stress relieved, round bar (22-32 mm)6205151540
Cold drawn, low temperature, stress relieved, round bar (22-32 mm)6555851130
Cold drawn, low temperature, stress relieved, round bar (16-22 mm)6906201235
Cold drawn, low temperature, stress relieved, round bar (50-75 mm)5855151025
Cold drawn, low temperature, stress relieved, round bar (32-50 mm)6205501030
Hot rolled, round bar (19-32 mm)5653101640
Turned, ground and polished, round bar (19-32 mm)8754052445
Request
Callback
Yes! I am Interested

Ck 50 Carbon Steel

Ck 50 Carbon Steel
  • Ck 50 Carbon Steel
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Metric7.85 g/cc
Imperial0.284 lb/in3
Thermal expansion16 - 17 e-6/K

CK-50 is a Fe-Cr-Ni alloy containing slightly more chromium and considerably more nickel than the CH-20 grade. The alloy is used provides good resistance to dilute sulfuric acid and resists many co rodents more effectively Than CF-8 type. The alloy is fully austenitic and contains chromium carbides throughout the matrix, which are put into solution by High temperature solution anneal, which also improves ductility and strength. The alloy should be solution Annealed to maximize corrosion resistance and after welding to prevent sensitization of the HAZ.

 

Applications:

  • Component parts for vehicles, shafts, bushings, crankshafts, connecting rods and parts for the machine building industry and steel for axes, knives, hammers etc.
  • Heat TreatmentSoft Annealing
  • Heat to 650-700°C, cool slowly.
  • Hardness after annealing
  • Max. 207 HB
  • Normalizing: Normalizing temperature (°C): 840-870°C.

 

Physical Properties:

QuantityValueUnit
Thermal expansion16 - 17e-6/K
Thermal conductivity16 - 16W/m.K
Specific heat500 - 500J/kg.K
Melting temperature1370 - 1400
Service temperature0 - 500
Density8000 - 8000kg/m3
Resistivity0.7 - 0.7Ohm.mm2/m


Thermal Properties:

PropertiesConditions
Treatment
Thermal Conductivity (W/m-K)42.7100
Specific Heat (J/kg-K)47750-100

Mechanical Properties:
PropertiesConditions
T (°C)Treatment
Density (×1000 kg/m3)7.7-8.0325
Poisson's Ratio0.27-0.3025
Elastic Modulus (GPa)190-21025
Tensile Strength (Mpa)115825oil quenched, fine grained, tempered at 425°C
Yield Strength (Mpa)1034
Elongation (%)15
Reduction in Area (%)53
Hardness (HB)33525oil quenched, fine grained, tempered at 425°C

 

 

Request
Callback
Yes! I am Interested

C55Mn75 Carbon Steel

C55Mn75 Carbon Steel
  • C55Mn75 Carbon Steel
Get Best Quote
Approx. Price: Rs 65 / KilogramGet Latest Price

Product Details:

Metric7.85 g/cm3
Imperial0.284 lb/in3
Reduction of area40%

Carbon steels are the steels having carbon as the major alloying element. They also contain up to 1.2% manganese and 0.4% silicon. In addition, the residual elements like copper, molybdenum, aluminium, chromium and nickel are present in these steels.

Applications:
  • Agricultural implements
  • Heavy machinery components
  • Wear-resistant parts
  • Ring-rolling tools
  • Battering tools
  • Hand tools
  • Springs

 

Heat Treatment:

  • Normalize at 1550° to 1625°F (843° to 885°C)
  • Full anneal at 1525° to 1600°F (829° to 871°C) before furnace cooling
  • Process anneal at 1100° to 1225°F (593° to 663°C) after cold working
  • Harden


Heat to 1450° to 1525°F (788° to 829°C):

  • Oil or water quench
  • Temper
  • May be oil or water quenched

Machinability:
    • Sulfured or chlorinated cutting oils for high-speed steel cutters
    • No oil for carbide-tip tools

      Grind carbide-tip tools:
      • 6-12° side rake
      • 2-8° back rake
      • 6-10° side and end relief
      • 8-12° end cutting-edge angle
      • 8-16° side cutting-edge angel
      • 1/32” nose radius

      Grind high-speed steel turning tools:
      • 8-12° side rake
      • 6-10° back rake
      • 7-9° side and end relief
      • 12-16° side cutting-edge angle
      • 8-14° end cutting-edge angle
      • Nose radius 10% of cut depth

      Workability:
      • Hot work 2200° to 1800°F (1204° to 982°C)
      • Intermediate annealing required for considerable cold working
      • Fully anneal when further cold work will follow extensive cold work


      Mechanical PropertiesShow 102550100 entriesSearch:

      PropertiesMetricImperial
      Tensile strength, ultimate660 MPa95700 psi
      Tensile strength, yield560 MPa81200 psi
      Modulus of elasticity190-210
      GPa
      29700-30458
      ksi
      Bulk modulus (typical for steel)140 GPa20300 ksi
      Shear modulus (typical for steel)80 GPa11600 ksi
      Poissons ratio0.27-0.300.27-0.30
      Elongation at break (in 50 mm)10%10%
      Reduction of area40%40%
      Hardness, Brinell197197
      Hardness, Knoop (converted from Brinell hardness)219219

       

      Request
      Callback
      Yes! I am Interested

      CK 60 Carbon Steel

      CK 60 Carbon Steel
      • CK 60 Carbon Steel
      Get Best Quote
      Approx. Price: Rs 65 / KilogramGet Latest Price

      Product Details:

      Modulus of elasticity210 [10^3x N/mm2]
      Density7.85[lbs/in3]
      DiameterUp to 16 MM

      CK60 steel is one of the higher carbon content (0.60%) steels. It is more difficult to fabricate than the lower carbon grades.

       

      Designation by Standards:

      • Brand Name: Ck 60
      • Mat No1.1221
      • DIN Ck65
      • EN -
      • AISI 1060


      Applications:

      • Shafts, bushings, connecting rods, Mechanical engineering components, agricultural hand tools, large forgings, springs, cold rolled strips.
      • Physical Properties(average values) at ambient temperature

      Soft Annealing:
      • Heat to 650-700°C, cool slowly in furnace. This will produce a maximum Brinell hardness of 241.
      • Hardening: Harden from a temperature of 800-830°C, 810-840°C followed by water or oil quenching. Normalizing
      • Normalizing temperature (°C): 820-850°C.
      • Tempering: Tempering temperature: 540-680°C. Forging
      • Hot forming temperature: 1100-850°C.
      • Machinability: Machinability of CK60 and all of the higher carbon steels is relatively poor.
      • CK60 rates at 55 to 60 % that of the AIS11112 steel which is considered 100% machinable Corrosion Resistance
      • This steel is not corrosion resistant, it will rust unless protected.

      Welding:
      • CK60 steel is weldable by all of the welding methods. However with its higher carbon content it is important to use both pre-heat at 150 to 260°C and post-heat at 590 to 650°C practice per an approved welding procedure.
      • Cold working is difficult even in the annealed condition although it may be done by conventional methods but requires greater force than the lower carbon steels.


      Chemical Composition:

      GradeMinMax
      Carbon, C0.550.65
      Manganese, Mn0.500.80
      Silicon, Si0.150.35
      Sulfur, S-.--0.50
      Phosphorous, P-.--0.50


      Mechanical Properties in Normalized Condition:

      Diameter (mm)0.2% proof stress (Wmm 2 )Tensile strength (Wmm 2 )Elongation (%)
      up to 1638071010
      17-4034067011
      41-10034067011
      101-16031065011
      161-25031065011

      Mechanical Properties in Quenched+Tempered Condition:
      Diameter0.2% proof stressTensile strengthElongation A5Reduction Z
      (mm)(Wmm 2 )(Wmm2)(%)(%)
      up to 16*580850 -10001125
      17-40520800-9501330
      41-100450750-9001435
      101- 160----

       

      Request
      Callback
      Yes! I am Interested

      IS2062GRB Carbon Steel

      IS2062GRB Carbon Steel
      • IS2062GRB Carbon Steel
      Get Best Quote
      Approx. Price: Rs 65 / KilogramGet Latest Price

      Product Details:

      Thickness1.50 mm-110.00 mm
      Width1250 / 1500 / 1800 / 2000 / 2500 mm
      Grade1079; SAE 1006;IS 2062/ Fe 410; SAE 1008; ASTM A 36; S5400

      The sheets and plates fabricated from steel alloy possesses the physical properties of density, reactivity, young’s modulus, and electrical and thermal conductivity almost same as those of its elements, but the engineering properties are much different.

        Those properties of steel alloy are:
        • High tensile strength
        • High shear strength
        • Free-Cutting Steel 12L14 =SUM24L/ 1215 =SUM23 / 1144 =SUM43

         

        Mechanical Properties:

        Mechanical PropertiesMetricImperial
        Tensile Strength, Ultimate400 - 550 MPa58000 - 79800 psi
        Tensile Strength, Yield250 MPa36300 psi
        Elongation at Break (in 200 mm)0.20.2
        Elongation at Break (in 50 mm)0.230.23
        Modulus of Elasticity200 GPa29000 ksi
        Bulk Modulus (typical for steel)140 GPa20300 ksi
        Poissons Ratio0.260.26
        Shear Modulus79.3 GPa11500 ksi
        Request
        Callback
        Yes! I am Interested

        S355J2G3 Carbon Steel

        S355J2G3 Carbon Steel
        • S355J2G3 Carbon Steel
        Get Best Quote
        Approx. Price: Rs 65 / KilogramGet Latest Price

        Product Details:

        Metric7.85 g/cm 3
        Imperial0.284 lb/in 3
        Thickness8mm-100mm

        Steel grade S355J2G3 is a low carbon, high strength structural steel which can be readily welded to other weldable steel. With its low carbon equivalent, it possesses good cold-forming properties. The plate is produced by fully killed steel process and supplied in n normalized or controlled rolling condition. S355J2G3 steel has its own features and its use is quite wide. Because of adding Cr, Cu and Ni, oxide layer forms stick firmly on the work piece surface. This oxide layer prevents further corrosion of the steel.


        Application:
        • Machinery parts, mobile equipment, crane, boom, chassis, buildings, bridges and most structural activities.


        The mechanical properties:

        GradeThickness(mm)Min Yield (Mpa)Tensile(MPa)Elongation(%)Min Impact Energy 
        S355J2/J2G38mm-100mm315Map-355Mpa450-630Mpa18-20%-2027J

        101mm-200mm285Mpa-295Mpa450-600Mpa0.18-2027J

        201mm-400mm275Mpa450-600Mpa0.17-2027J


        Heat treatment conditions:

        Quenching Temperature, 0CCooling mediumTempering Temperature, 0CNormalizing
        temperature, 0C
        ---890


        Comparison of steel grades:

        JUS

        (.0561, .0562, .0563)

        DIN

        St52-3N

        BS

        50D

        GOST

        -

        AISI

        -

        UNI

        -

        NF

        -

         

        Request
        Callback
        Yes! I am Interested

        ASTMA105 Carbon Steel

        ASTMA105 Carbon Steel
        • ASTMA105 Carbon Steel
        Get Best Quote
        Approx. Price: Rs 65 / KilogramGet Latest Price

        Product Details:

        Tensile Strength min70,000 psi (485 MPa]
        Min Yield Point36,000 psi [250 MPa]
        Reduction of area min30% min

        ASTM A105 is the Standard Specification for Carbon Steel Forgings for Piping and fittings Applications. The forged carbon steel piping components manufactured under the A 105 steel specification are used in pressure systems operating at ambient- and higher-temperatures.

        Quick View System:
        • The sum of copper, nickel, chromium, molybdenum and vanadium shall not exceed 1.00%.
        • The sum of chromium and molybdenum shall not exceed 0.32%.
          Note: For each reduction of 0.01% below the specified carbon maximum (0.35%), an increase of 0.06% manganese above the specified maximum (1.05%) will be permitted up to a maximum of 1.35%.
        • A105 Available Classes
        • Class 150, Class 300, Class 400, Class 600, Class 900, Class 1500 and Class 2500.

        Principal Design Features:
        • A 105 is an ASTM specification dealing with forged carbon steel piping components.
        • The steel alloy involved is a low carbon, manganese and silicon containing steel similar to AISI 1330, but with lower manganese content.

        Applications:
        • This ASTM specification covers carbon steel forgings for piping applications such as flanges and fittings

        Machinability:
        • Machinability is good as for any of the low alloy steels.

        Heat Treatment:
        • Heat treatment is not required except for flanges or piping components as called out in ASTM A 105/A section 5.1.
        • When heat treatment is required it consists of normalizing at 1550 to 1700 F and air cooled.
        • Quenching direct from the forging heating shall be followed by a temper at 1100 F and air cool.

        Annealing:
        • Annealing may be done by first allowing the forged parts to cool to below 1000 F and then reheat to between 1550 and 1700 F followed by slow furnace cooling.

        Forging:
        • This is a forging alloy that would be forged at temperatures in the range of 2200 to 1700 F followed by quenching and tempering or normalizing.

         

        Chemical Composition:

        ElementMinMax
        Carbon, C-.--0.35
        Manganese, Mn0.601.05
        Silicon, Si0.100.035
        Nickel, Ni-.--0.04
        Molybdenum, Mo-.--0.12
        Chromium,Cr-.--0.03
        Vanadium, V-.--0.08
        Copper-.--0.04
        Sulfur, S-.--0.04
        Phosphorous, P-.--0.035

        Mechanical Properties:
        Property 
        Tensile Strength, min:70,000 psi (485 MPa]
        Min. Yield Point:36,000 psi [250 MPa]
        Reduction of area, min:30% min
        Hardness, HB, max187
        Request
        Callback
        Yes! I am Interested

        EN43B Carbon Steel

        EN43B Carbon Steel
        • EN43B Carbon Steel
        Get Best Quote
        Approx. Price: Rs 65 / KilogramGet Latest Price

        Product Details:

        MaterialCarbon Steel
        Silicon0.35%
        Carbon0.50%

        Carbon spring steel which is supplied in round bar, hexagon, flat and also as spring steel plate and sheet. Plate can be flame cut to your requirements with normalising recommended for this spring steel grade. Bar can be cut to your required lengths. Spring steel plate and sheet can be flame cut or guillotine cut to your requirements. Spring steel strip is available in coil, slit and cut to length. Spring steel, as its name suggests, is most commonly used in the manufacture of springs. When hardened and tempered (as supplied, or heat treated by the customer) it offer excellent spring characteristics. We welcome export enquiries for spring steel. Please contact our sales office and consult our  shipping policy for details. If you do no find the spring steel specification you require on our web site please contact our sales team who may be able to assist you with your enquiry.

        Form of Supply:
        • Carbon spring steel strip, plate and sheet is supplied in the hardened and tempered and annealed condition. Stainless spring steel is available as strip.
        • Spring steel strip is commonly supplied in coil cut to your requirements.
        • Bar is available in carbon, chrome vanadium and silicon manganese spring steel types.
        • Supplied in full bar lengths or cut as one offs or multiple cut pieces.
        • Medium carbon spring steel grades can be flame cut to your requirements.
        • Profiles are commonly normalised or stress relieved to alleviate any hard edges which may have occured during flame cutting.


        Chemical composition:

        ElementMin %Max %
        Carbon, C0.450.50
        Manganese, Mn0.701.00
        Silicon, Si0.050.35
        Nickel, Ni-.---.--
        Molybdenum, Mo-.---.--
        Chromium,Cr-.---.--
        Sulfur, S-.--0.05
        Phosphorous, P-.--0.05
        Request
        Callback
        Yes! I am Interested

        15C8 Carbon Steel

        15C8 Carbon Steel
        • 15C8 Carbon Steel
        Get Best Quote
        Approx. Price: Rs 65 / KilogramGet Latest Price

        Product Details:

        Tensile strength ultimate965-1030 MPa
        Tensile strength yield827-862 MPa
        Compressive strength862 MPa

        The term mild steel applies to all low carbon steel that does not contain any alloying elements in its makeup and has a carbon content that does not exceed 0.25%. The term “mild” is used to cover a wide range of specifications and forms for a variety of steel. Mild steel is used in mechanical engineering applications for parts that will not be subject to high stress. When in its bright cold drawn condition the steel is able to endure higher levels of stress, particularly on smaller diameters. Compared to normal mild steel, bright mild steel provides tighter sectional tolerances, increased straightness, and a much cleaner surface. The main advantage of cold drawn steel is that steel can be bought closer to the finished machine size, providing reduce machining costs. Another benefit of bright steel bars is a marked increase in physical strength over hot rolled bars of the same section. It has since been replaced by steels that have a tighter chemical analysis. 15c8 mild steel is now a general purpose steel that is suitable for welding, can be case-hardened and is good for general machining. 15C8 is generally used in engineering applications that will not be heavily stressed. A general purpose steel suitable for mechanical and allied engineering applications that will not be heavily stressed. Machinability and weldability are both good and it can be case-hardened.

        Quick View System:
        • Machinability – 100
        • Weldability – Good
        • Hardenability – Poor
        • Selection Guide And Usage Examples – General purpose engineering
        • Heat Treatments
        • Hardening, tempering, annealing, normalising, stress relieving, solution annealing

        Testing:

        • In addition to sourcing your forged steel products we can also arrange comprehensive testing: Metallurgical and Mechanical.
        • This includes non destructive testing: Ultrasonic Testing, MPI (Magnetic Particle Inspection), dye-penetrant inspection. Mechanical testing
        • Tensile, Izod, Charpy, Stress Rupture, Hardness.
        • Advantages of forged steel components

          Costs:
          • The forging process is a cost trade-off between the initial setup cost of the dies and tools, and the recurring costs of manufacturing parts.
          • Therefore forgings become more cost effective when larger production runs are required.

          Strength:
          • There are also metallurgical advantages to forging a steel component.
          • Because the metal is shaped during the process the internal grain deforms and follows the general shape of the piece.
          • This results in a final product with better strength characteristics that could be achieved through machining alone.

           

          Chemical Composition:

          PropertiesMetricImperial
          Hardness, Brinell (typical)30033
          Hardness, Rockwell C (typical)3030
          Tensile strength, ultimate965-1030 MPa140000-150000 psi
          Tensile strength, yield827-862 MPa120000-125000 psi
          Elongation at break (in 50 mm (2"))20.0%20.0%
          Compressive strength862 MPa125000 psi
          Charpy impact (V-Notch)27.1-33.9 J20.0-25.0 ft-lb
          Poisson's ratio0.27-0.300.27-0.30
          Elastic modulus190-210 GPa27557-30457 ksi

          Mechanical Properties:
          ConditionTensile Strength MPa Min.Yield Strength MPa Min.Elongation %
          Cold drawn56044010
          Turned & Polished43021521
          Request
          Callback
          Yes! I am Interested

          20C8 Carbon Steel

          20C8 Carbon Steel
          • 20C8 Carbon Steel
          Get Best Quote
          Approx. Price: Rs 60 / KilogramGet Latest Price

          Product Details:

          ApplicationConstruction, Industrial
          MaterialCarbon Steel
          Grade20C8

          We are engaged in offering the finest quality 20C8 Carbon Steel
          Request
          Callback
          Yes! I am Interested

          EN24 Round Bar

          EN24 Round Bar
          • EN24 Round Bar
          Get Best Quote
          Approx. Price: Rs 80 / KilogramGet Latest Price

          Product Details:

          Material GradeEN 24

          EN24 steel bar manufacturers and stockist

          Request
          Callback
          Yes! I am Interested
          X

          Explore more products

          EN 19 Alloy Steel
          EN 19 Alloy Steel
          Get Best Quote
          Forging Steel CK 30
          Forging Steel CK 30
          Get Best Quote
          En Series Steel 8
          En Series Steel 8
          Get Best Quote
          EN 353 Series Steel
          EN 353 Series Steel
          Get Best Quote
          Die Steel
          Die Steel
          Get Best Quote


          Reach Us
          Saket Khaitan (Partner)
          Ajod Dairy Road, Opposite Gravity House, Near Keval Kanta Gujarat Bottling, Rakhial
          Amraiwadi, Ahmedabad- 380023, Gujarat, India



          Call Us

          Share Us

          F GT L


          Send E-mailSend SMS